Vol 17, No 2 (2013) > Articles >

Improvement in Performance of ZnO based DSC Prepared by Spraying Method

Rangga Winantyo 1 , Devinda Liyanage 1 , Kenji Murakami 2

Affiliations:

  1. Graduate School of Science and Technology, Shizuoka University, 3-5-1 Johoku, Naka-ku, Hamamatsu 432-8011, Japan
  2. Research Institute of Electronics, Shizuoka University, 3-5-1 Johoku, Naka-ku, Hamamatsu 432-8011, Japan

 

Abstract:

This paper reports the effect of TiCl4 on the performance of ZnO based DSC. ZnO was used due to its stability against photo-corrosion  and  photochemical  properties  similar  to  TiO2.  Thin  films  of  nanocrystalline  ZnO  were  deposited  on transparent conducting oxide glass using spray  method. The ZnO  films  were treated using TiCl4. The cell’s efficiency was found to be 2.5% with TiCl4 post-treatment and 1.9% without TiCl4 post-treatment.

Keywords: DSSC, ZnO, TiCl4
Published at: Vol 17, No 2 (2013) pages: 77-78
DOI:

Access Counter: 1037 views, 640 PDF downloads, .

Full PDF Download

References:

M.D. McCluskey, S.J. Jokela, Physica B. 401-402 (2006) 355.

G.V. Irene, L.C. Monica, Energ. Environ. Sci. 2 (2008) 23.

J. Halme, Master Thesis, Department of Engineering Physics and Mathematics, Helsinki University of Technology, Finland, 2002.

R.S. Mane, W.J. Lee, H.M. Pathan, S.H. Han, J. Phys. Chem. B. 109/51 (2005) 24254.

N. Sakai, N. Kawashima, T.N. Murakami, Chem. Lett. 40 (2011) 162.

J.Z. Marinho, F.C. Romeiro, S.C.S. Lemos, F.V. Motta, C.S. Riccardi, M.S. Li, E. Longo, R.C. Lima, J. Nanomater. 2012 (2012) 1. DOI:10.1155/2012/427172.